This document supersedes the October edition of DNV-RP-F The purpose of the revision of this service document is to comply with the new DNV GL. If any person suffers loss or damage which is proved to have been caused by any negligent act or omission of Det Norske Veritas, then Det Norske Veritas shall. DNV-RP-F DESIGN OF DUPLEX STAINLESS STEEL SUBSEA EQUIPMENT EXPOSED TO CATHODIC PROTECTION.

Author: Vuran Tagore
Country: Benin
Language: English (Spanish)
Genre: Finance
Published (Last): 19 November 2017
Pages: 499
PDF File Size: 5.23 Mb
ePub File Size: 16.30 Mb
ISBN: 856-8-31722-942-9
Downloads: 39291
Price: Free* [*Free Regsitration Required]
Uploader: Mikacage

Typical uses are short flowlines, welded hubs and flanges, manifolds, towheads, flowbases, sensors and valves. Log in to your subscription Username.

Hydrogen induced stress cracking using DNV-RP-F – SDEA Solutions

Proceedings of an international conference Subsea Controls and Data Acquisition ‘ This CP results in hydrogen charging of the duplex stainless steel, either at uncoated locations or, in locations where the coating has lost integrity. As subsea facilities are protected from seawater corrosion by cathodic protection CPS DSS components are exposed to hydrogen uptake, especially when a coating system is not in place or has failed at a certain location.

  2N EASYGATE GSM GATEWAY PDF

Proceedings of an international conference Oceanology: Proceedings of an international conference Diverless and Deepwater Techology: Full scale test validation of this approach is limited. Advanced search Show dnc help. Instead, the industry assumes that hydrogen charging will happen and relies instead on design approaches that avoid equipment being exposed to stresses or strains exceeding the nominal thresholds for HISC.

DNVGL-RP-F Duplex stainless steel – design against hydrogen induced stress cracking – DNV GL

Ferritic-austenitic duplex stainless steels DSS are often used to manufacture subsea components for their high strength associated with a good corrosion resistance. A comprehensive test program is described quantifying the HISC performance of retrieved superduplex stainless steel subsea components and, comparing the actual performance against the limits derived following DNV RP F Rock Mechanics Symposium and 5th U.

Proceedings of an International Conference Submersible Technology: Whilst mitigations such as increased less negative CP potential, tailored microstructure g112 high-reliability coatings can be considered, these are challenging and are rarely a complete barrier to the threat.

Peer reviewed only Published between: However, whilst these materials are advantageous for managing internal corrosion, they still require external cathodic protection CP to prevent localized corrosion in seawater at typical operating temperatures.

  BONOLOTA SEN POEM BANGLA PDF

To facilitate this comparison, comprehensive material characterization, small, intermediate and full scale environmental-mechanical testing, and finite element analyses were conducted.

Sheriff’s Encyclopedic Dictionary of Applied Geophysics, fourth edition. About us Contact us Help Terms of use.

Publishers Content Coverage Privacy. Ferritic-austenitic duplex and superduplex stainless steels DSSs and SDSSs are an attractive option for subsea equipment and connecting spools, in which the internal corrosion threats can be difficult to manage, using corrosion inhibition and in-line inspection. In the presence of a critical hydrogen concentration, all duplex and super duplex stainless steels are susceptible to hydrogen embrittlement, via a cracking mechanism commonly referred to as HISC: ABSTRACT Ferritic-austenitic duplex dp superduplex stainless steels DSSs and SDSSs are an attractive option for subsea f1112 and connecting spools, in which the internal corrosion threats can be difficult to manage, using corrosion inhibition and in-line inspection.